Non-shrink, high strength, free flowing & self leveling, nonmetallic, chloride free cementitious grout for general purpose grouting of static loads, as well as centrifugal and rotary machines in cement, textile, paper, steel industries etc.

Attains 450 kg/cm compressive strength at 28 days.

Expansion : 0.8% to 1.5%, 2 Density-1800 Kg/cm

Water powder ratio : Pourable 0.17, Flowable - 0.19.

Non-shrink, high strength, free flowing & self leveling, nonmetalic, chloride free cementitious grout for general purpose, grouting for dynamic load. Freely flows under base plates and bolt pockets. High, early & ultimate strength.

Attains 650 Kg/cm compressive strength at 28 days.

Expansion : 0.8% to 1.5%

Density : 1900 Kg/cm Water powder ratio: Pourable 0.16, Flowable - 0.18.

Super plasticiser, shrinkage compensating, iron free, chloride free grout additive. Produces easy flowing cohesive grout, attains higher strength. Ideal for static load.

Dosage : 250 gms. Per 50 Kg. Of cement.

Compressive strength : 350 2 Kg/cm with 1:1 cement: sand.

High strength, non-shrink, three pack, free flowing, high performance epoxy grout. A unique epoxy grout system even for running industry with minimum production shut down. Ideal for very heavy dynamic loads like heavy duty rails, machineries, compressors, dowel bars, studs etc.

High tensile & flexural strength 2 attains 970 kg/cm compressive strength in 7 days.

Low viscosity, high penetrating, ultra high strength, tow part, solvent free, epoxy based injection grout. Attains high early and ultimate strength.

Ready to use ultra high strength injection cementitious grout for cracks in concrete brick work and masonry. Suitable for damp or dry surface. Attains 50 N/m 2 m compressive strength at 28 days.